Raise3D Premium ASA - 1.75mm - 1 kg - Black
- Artikelnr. 25806
- Varianten Id 7139
- EAN 6970240722373
- Hersteller Nr. [S]5.11.01052A01
| Basisdaten | |
| Filament Typ | ASA |
| Durchmesser | 1,75 mm |
| Toleranz | 0,05 mm |
| Gewicht | 1,00 kg |
| Länge | 378 m |
| Druck Parameter | |
| Empfohlene minimale Drucktemperatur | 240 ºC |
| Empfohlene maximale Drucktemperatur | 260 ºC |
| Empfohlene Min. Betttemperatur | 75 ºC |
| Empfohlene Max Bed Temp | 95 ºC |
| Empfohlene Min. Druckgeschwindigkeit | 30 mm/s |
| Empfohlen Max Print Speed | 50 mm/s |
| Empfohlener Rückzug Min | 1 mm |
| Empfohlener Rückzug Max | 3 mm |
| Allgemein | |
| Spezifische Dichte | 1,1 g/cm3 ASTM D792 |
| Temperatur | |
| Vicat-Erweichungstemp. | 105,3 °C ASTM D1525 |
| Biegefestigkeit | |
| Biegefestigkeit | 73,4 MPa ASTM D790 |
| Biegemodul | 3206 MPa ASTM D790 |
| Sonstiges | |
| Schlagzähigkeit | 10,3 KJ/m2 ASTM D256 |
Weitere passende Prdoukte
- Schwarz
- 1.75mm
- 1 kg
- Schwarz
- 1.75mm
- 1 kg
- Weiss
- 1.75mm
- 1 kg
- Weiss
- 1.75mm
- 1 kg
- Grau
- 1.75mm
- 1 kg
- Grau
- 1.75mm
- 1 kg
- Schwarz
- 1.75mm
- 3 kg
- Schwarz
- 1.75mm
- 3 kg
- Army Green
- 1.75mm
- 1 kg
- Army Green
- 1.75mm
- 1 kg
- Rot
- 1.75mm
- 1 kg
- Rot
- 1.75mm
- 1 kg
- Polymaker Teal
- 1.75mm
- 1 kg
- Polymaker Teal
- 1.75mm
- 1 kg
- Schwarz
- 1.75mm
- 5 kg
- Schwarz
- 1.75mm
- 5 kg
- Blau
- 1.75mm
- 1 kg
- Blau
- 1.75mm
- 1 kg
- Gelb
- 1.75mm
- 1 kg
- Gelb
- 1.75mm
- 1 kg
- Army Brown
- 1.75mm
- 1 kg
- Army Brown
- 1.75mm
- 1 kg
- Weiss
- 1.75mm
- 3 kg
- Weiss
- 1.75mm
- 3 kg
- Grun
- 1.75mm
- 1 kg
- Grun
- 1.75mm
- 1 kg
- Grau
- 1.75mm
- 3 kg
- Grau
- 1.75mm
- 3 kg
- Lila
- 1.75mm
- 1 kg
- Lila
- 1.75mm
- 1 kg
- Orange
- 1.75mm
- 1 kg
- Orange
- 1.75mm
- 1 kg
- Natural
- 1.75mm
- 1 kg
- Natural
- 1.75mm
- 1 kg
- Schwarz
- 1.75mm
- 750g
- Schwarz
- 1.75mm
- 750g
- Natural
- 1.75mm
- 3 kg
- Natural
- 1.75mm
- 3 kg
- Natural
- 1.75mm
- 750g
- Natural
- 1.75mm
- 750g
- Schwarz
- 2.85mm
- 750g
- Schwarz
- 2.85mm
- 750g
- Blau
- 1.75mm
- 3 kg
- Blau
- 1.75mm
- 3 kg